405 BA finish high quality stainless steel strip manufacture, 405 stainless steel round bar
| Al | C | Mn | P | S | Cr | Si | Ni | N | Cu |
| 0.10-0.30 | max. 0.08 | max. 1.00 | max. 0.040 | max. 0,030 | 11.5 – 14.5 | max 1.00 | max, 0.5 | – | – |
| Al | C | Mn | P | S | Cr | Si | Ni | N | Cu |
| 0.10-0.30 | max. 0.08 | max. 1.00 | max. 0.040 | max. 0.030 | 11.5 – 14.5 | max 1.00 | max 0.60 | – | – |
| Al | C | Mn | P | S | Cr | Si | Ni | N | Cu |
| 0.10-0.30 | max. 0.08 | max. 1.00 | max. 0.040 | max. 0.015 | 12.0 – 14.0 | max 1.00 | max 0.60 | – | – |
| Material Grade | Material Number | Tensile StrengthRmN/mm² ksi(MPa) min |
Yield StrengthRp0.2%N/mm²(MPa) min |
Elongation(%) | BrinellHardness Testmax | RockwellHardness Testmax |
| TP405 | S40500 | 60 (415) | 30 (205) | 20 | 207 | 95 |
| Material Grade | Material Number | Tensile Strength Rm N/mm² ksi(MPa) min |
Yield Strength Rp0.2% N/mm²(MPa) min |
Elongation (%) |
| TP 405 | 1.4002 | 400-600 | 230 | 17 |
Commonly used for annealing boxes, steam nozzles, quenching racks, partitions and other fabrications that cannot be annealed after welding.
Soft and ductile, 405 can be easily machined using most standard practices. Experienced machinists comment that 405 machines similarly to 4130 alloy steel.
405 can be easily spun, drawn and formed using common forming procedures.
405 can be welded using shielded fusion and resistance techniques. Oxyacetylene welding is not recommended. Use 405 Cb electrodes that contain columbium rather than aluminum to control hardening. Post weld annealing will maximize ductility.
Soak at 1500-1600°F(817-871°C) and then quickly increase to 1900-2050°F(1038-1121°C). Do not remain at this temperature as the result will be excessive grain growth. Do not work below 1500°F(816 °C). After forging, air cool and anneal.
Soak at 1200-1400°F(649-760°C), air cool.
While this alloy does not respond appreciably to heat treatment, soaking at 1800-1850°F(982-1010°C) followed by oil quenching will increase mechanical properties.
| C | Mn | Si | P | S | Cr | |
| Min | 11.5 | |||||
| Max | 0.15 | 0.50 | 1.00 | 0.04 | 0.03 | 13.5 |
| Condition | Tensile Strength, PSi | Yield Strength 0.2% PSi | Elongation % | Reduction of are % | Hardness HB |
| A | 115,000 | 241 | |||
| HT | 120,000 | 90,000 | 12 | 40 | 269 |
Commonly used for annealing boxes, steam nozzles, quenching racks, partitions and other fabrications that cannot be annealed after welding.
Soft and ductile, 405 can be easily machined using most standard practices. Experienced machinists comment that 405 machines similarly to 4130 alloy steel.
405 can be easily spun, drawn and formed using common forming procedures.
| 405 stainless steel plate sizes and specifications | |
| Grade | 405 |
| Cold rolled stainless steel plate | Thickness: 0.3mm- 16.0mm, Width: 1000mm - 2000mm, Length: as requirements, Surface: 2B/BA/SB/8K/HL/1D/2D etc |
| Hot rolled stainless steel sheet | Thickness: 3.0mm - 300mm, Width: 1000mm - 3000mm Length: as requirements, Surface: No.1/pickling |
| Standard |
ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303, BS 1449, DN17441, G4305 |
| Stainless steel plate | Thickness: 8.0mm - 300mm, Width: 1000mm - 3000mm Length: as requirements, Surface: No.1/pickling |
| 405 stainless steel strip sizes and specifications | |
| Grade | 405 |
| Cold rolled stainless steel strip | Thickness: 0.3mm- 3.0mm, Width: 5mm - 900mm, Surface: 2B/BA/SB/8K/HL/1D/2D etc |
| Hot rolled stainless steel strip | Thickness: 3.0mm - 16mm, Width: 10mm - 900mm Surface: No.1/pickling |
| Stainless steel foil | Thickness: 0.02mm- 0.2mm, Width: Less than 600mm, Surface: 2B |
| Standard |
ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303, BS 1449, DN17441, G4305 |
| 405 stainless steel coil sizes and specifications | |
| Grade | 405 |
| Cold rolled stainless steel coil | Thickness: 0.3mm- 3.0mm, Width: 1000mm - 2000mm,
Surface: 2B/BA/SB/8K/HL/1D/2D etc |
| Hot rolled stainless steel coil | Thickness: 3.0mm - 16mm, Width: 1000mm - 2000mm
Surface: No.1/pickling |
| Standard |
ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303, BS 1449, DN17441, G4305 |
| 405 stainless steel pipe sizes and specifications | |
| Grade | 405 |
| Stainless steel seamless pipe | Outside diameter: 4.0 - 1219mm, Thickness: 0.5 -100mm,
Length: 24000mm |
| Stainless steel welded pipe | Outside diameter: 6.0 - 2800mm, Thickness: 0.3 -45mm,Length: 18000mm |
| Stainless steel capillary pipe | Outside diameter: 0.4 - 16.0mm, Thickness: 0.1 -2.0mm, Length: 18000mm |
| Stainless steel welded sanitary pipe | Outside diameter:8.0- 850mm, Thickness: 1.0 -6.0mm |
| Stainless steel seamless sanitary pipe | Outside diameter: 6.0- 219mm, Thickness: 1.0 -6.0mm |
| Stainless steel square pipe | Side Length: 4*4 - 300*300mm, Thickness: 0.25 - 8.0mm, Length: 18000mm |
| Stainless steel rectangular pipe | Side Length: 4*6 - 200*400mm, Thickness: 0.25 - 8.0mm, Length: 18000mm |
| Stainless steel coil pipe | Outside diameter: 0.4 - 16mm, Thickness: 0.1 - 2.11mm |
| Standard |
American Standard: ASTM A312, ASME SA269, ASTM A269, ASME SA213, ASTM A213 ASTM A511 ASTM A789, ASTM A790, ASTM A376, ASME SA335, B161, SB163, SB338, SB667/668 Germany Standard: DIN2462.1-1981, DIN17456-85, DIN17458-85· European Standard: EN10216-5, EN10216-2 Japanese Standard: JIS G3463-2006, JISG3459-2012 Russian Standard: GOST 9941-81 |
| 405 stainless steel profile sizes and specifications | |
| Grade | 405 |
| Specification | EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO |
| Standard | ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 . |
| Stainless steel round Bar | Diameter: 2mm - 600mm |
| Stainless steel bright Bar | Diameter: 2mm - 600mm |
| Stainless steel hex Bar | Dimension: 6mm - 80mm |
| Stainless steel square bar | Dimension: 3.0 - 180mm
|
| Stainless steel flat bar | Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm |
| Stainless steel angle bar | as requirements |
| Length | Normally 6m, or produce as requirements |
| Surface | Black, Bright. Peeled and Polished, Solution annealed. |
| Delivery condition | cold drawn, hot rolled, forged, grinding, centerless grinding |
| Tolerance | H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients’ requirements |